강자성 소자 (Ferromagnetic Components) vs 훼리자성 화합물 (Ferrimagnetic compounds)

1. magnetic material (자성체)
relative permitivity, μ_r= 1+χ_m
- Diamagnetic    (반자성체), μ_r≲1 일 때 (χ_m is a very small negative number)
- Paramagnetic  (상자성체), μ_r≳1 일 때 (χ_m is a very small positive number)
- Ferromagnetic (강자성체), μ_r>>1 일 때 (χ_m is a large positive number)

* diamagnetism arises mainly from the orbital motion of the electrons within an atom
* paramagnetism is mainly from the magnetic dipole moments of the spinning electrons.
* magnetic susceptibility (χ_m)
  - diamagnetic materials : the order of -10^-5
     (copper, germanium, silver, gold)
  - paramagnetic materials : the order of 10^-5
     (aluminum, magnesium, titanium, tungsten)

2. Ferromagnetic materials (강자성 소자)

- Iron (철)
- steel (강철)
- 코발트


3. Ferrimagnetic compounds (훼리자성 화합물)

- YIG (yttrium iron garnet)
- ferrite (페라이트)
     : 산화철에 앨류미니엄, 코발트, 망간, 니클과 같은 여러가지 다른 종류의 원소를 혼합한 자성체
     : 투자율이 높고, 외부 자계에 의해 내부의 자구 정렬이 변화한다.
     : N, S극이 결정된 자석이 아니라 일정 크기 이상의 외부자력을 가하면 내부의 자구방향이 바뀐채
      고정시킬 수 있다.
     : 냉장고의 고무자석,
     : 전자파 차폐용/ 도선의 EMI 억제용 - 전파무반향실, 스텔스의 전면, 중계기 기지국 내부


-- high resistivity (very low conductivity)
     : coores for FM antennas, high frequency transforms, phase shifters 등으로 사용
-- significant amount of anisotropy at microwave frequency
     :  자기적 비등방성은 DC magnetic bias field가 인가됨으로써 유도된다.
     :  비등방성을 이용하여 isolator, circulator, gyrator 등을 제작한다.

---

결론 : magnetic material ⊃ ferromagnetic ⊃ Ferrimagnetic